316L Stainless Steel Bar
316L stainless steel, similar to 316 stainless steel, has a lower amount of carbon of no more than 0.03% in its composition. This is meant to reduce the risk of carbon precipitation, to make a better choice for welding to achieve maximum corrosion resistance.
- Product Description
- Spot Warehouse
- Product Inspection
- Product Measurement
- Product Packaging
-
- Commodity name: 316L Stainless Steel Bar
316L stainless steel, similar to 316 stainless steel, has a lower amount of carbon of no more than 0.03% in its composition. This is meant to reduce the risk of carbon precipitation, to make a better choice for welding to achieve maximum corrosion resistance.
316L Stainless Steel Bar Description
316L stainless steel bar just has a lower carbon content than 316 stainless steel bar and it is used mostly for welding purposes. The lower carbon content greatly lowers the precipitation of carbides in the heat-affected zone close to the weld, and such precipitation is likely to lead to intergranular corrosion of stainless steel in certain settings. Basically, their is no need to anneal weld joints prior to using the completed metal form using 304L, which helps save time and effort. 316L stainless steel bar is one of the most widely used stainless steel bars like 304, with better corrosion resistance. 316L stainless steel bar also has high temperature resistance that can go with up to 1000 degrees. Lastly, 316L stainless steel has stronger rust resistance than 200 series stainless steel materials.
Product ParametersProduct Name
316L Stainless Steel Bar
Type
Steel Bar
Outer Diameter
Round Bar
4mm-500mm
Hexagon Bar
18mm-57mm (11/16″ to 2-3/4″)
Square Bar
18mm-47mm (11/16″ to 1-3/4″)
Flat Steel
1/2 "to 10", Thickness: 2mm-150mm, Can provide customized
Length
1-6 meters, Length can be customized
Standard
ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface
Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc.
Scope of Application
Stainless steel bars are used in a variety of industries such as shipbuilding,
Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement,
Heavy earthmoving equipment and construction, etc.
Chemical Composition
C
Si
Mn
Cr
Ni
S
P
Mo
≤ 0.03
≤1.0
≤ 2.0
16.0～18.0
10.0～14.0
≤ 0.03
≤ 0.045
2.0～3.0
Mechanical Properties
Tensile Strength Kb (MPa)
Yield Strength σ0.2 (MPa)
Elongation D5 (%)
Hardness
≥480
≥177
≥ 40
≤ 187HB;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³)
Modulus of Elasticity(Gpa)
Coefficient of Thermal Expansion(10-6/°C)
Coefficient of Thermal Conductivity(W/m*K)
Resistivity(ΜΩ. cm)
7.99
193
16.0
16.2
74
-
316L Stainless Steel Bar - Stock Warehouse
-
316L Stainless Steel Bar - Product Inspection
Tensile Strength Testing Tensile Strength Testing Physical Performance Testing Chemical Composition Testing 
Inspection Hardness Testing Spectral Detection Mechanical Properties -
316L Stainless Steel Bar - Product Measurement
Outer Diameter Measurement Outer Diameter Measurement Outer Diameter Measurement Outer Diameter Measurement -
316L Stainless Steel Bar - Product Packaging
Baowu Special steel
Your reliable steel supplier
Baowu Special steel has 10+ warehouses with ready stock. The annual supply capacity is approximately 10 million tons. It has 10 years of experience in large-scale project supply. The customer reorder rate reaches 86%. We ensure quality and quantity, provide material certificates, and will refund if the products are not qualified, so please be assured the purchase.
Get A Quote
3D Virtual Pavilion
Douyin Official Media
Flagship Micro Mall
WeChat Public Number
CONTACT US
Mobile: +86-13256761911
Wechat: +86-13256761911
Whatsapp: +86-13256761911
Tel : +86-531-86666666
Address : 1-709-1 Ginza Jingdu International Plaza, No.66 Shunhe East Street, Luoyuan Street, Shizhong District, Jinan City, Shandong Province
Baowu Special steel Products (Shandong) Co., Ltd.