316L Stainless Steel Pipe
316L stainless steel has a lower proportion of carbon in its composition, the amount of carbon cannot go over 0.03%. This lowers the chance of carbon precipitation, making it an ideal option for welding to ensure maximum corrosion resistance.
- Product Description
- Spot Warehouse
- Product Inspection
- Product Measurement
- Product Packaging
-
- Commodity name: 316L Stainless Steel Pipe
316L stainless steel has a lower proportion of carbon in its composition, the amount of carbon cannot go over 0.03%. This lowers the chance of carbon precipitation, making it an ideal option for welding to ensure maximum corrosion resistance.
316L Stainless Steel Pipe Description
316L stainless steel pipe has a lower carbon content than 316 stainless steel pipe and is used when welding is needed. The lower carbon content greatly reduces the precipitation of carbides in the heat-affected zone close to the weld, and the precipitation of carbides is strongly associated with intergranular corrosion of stainless steel in some environments. Basically, there is no need to anneal weld joints prior to using the completed metal form. 316L stainless steel pipe is the second most prevalent stainless steel after 304, and it has better corrosion resistance than 304. High temperature resistance is also better, up to 1000 degrees. 316L stainless steel plate is a universal stainless steel material, with better rust resistance than 200 series stainless steel material. 316L stainless steel pipe is widely used in the chemical industry because of its excellent corrosion resistance.
Product ParametersProduct Name
316L Stainless Steel Pipe
Type
Steel Pipe
Outer diameter
Round Tube
4mm-200mm
Square Tube
10*10mm-100*100mm
Rectangular Tube
10*20mm-50*100mm
Wall Thickness
0.6mm-6.0mm
Length
1-6 meters, Length can be customized
Standard
ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface
Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc.
Scope of Application
Common applications for stainless steel pipes include food processing,
Textile operations, Breweries, Water treatment plants, Oil and gas processing,
Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc.
Certificate
ISO, SGS, BV, etc.
Production Technology
Hot Rolling, Cold Rolling
Edge Processing
Edging, Trimming
Chemical Composition
C
Si
Mn
Cr
Ni
S
P
Mo
≤ 0.03
≤1.0
≤ 2.0
16.0～18.0
10.0～14.0
≤ 0.03
≤ 0.045
2.0～3.0
Mechanical Properties
Tensile Strength Kb (MPa)
Yield Strength σ0.2 (MPa)
Elongation D5 (%)
Hardness
≥480
≥177
≥ 40
≤ 187HB;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³)
Modulus of Elasticity(Gpa)
Coefficient of Thermal Expansion(10-6/°C)
Coefficient of Thermal Conductivity(W/m*K)
Resistivity(ΜΩ. cm)
7.99
193
16.0
16.2
74
-
316L Stainless Steel Pipe - Stock Warehouse
-
316L Stainless Steel Pipe - Product Inspection
Tensile Strength Testing Tensile Strength Testing Physical Performance Testing Chemical Composition Testing 
Inspection Hardness Testing Spectral Detection Mechanical Properties -
316L Stainless Steel Pipe - Product Measurement
Pipe measurement